Influence of Vanadium Tailings from Stone Coal on Sintering Brick for Building

Zhang Hailing

doi:10.3969/j.issn.1000-6532.2023.02.029

2023 No. 2

Article Contents

Article navigation > Multipurpose Utilization of Mineral Resources > 2023 > 44(2): 191-196

Next Article Previous Article

Zhang Hailing. Influence of Vanadium Tailings from Stone Coal on Sintering Brick for Building[J]. Multipurpose Utilization of Mineral Resources, 2023, 44(2): 191-196. doi: 10.3969/j.issn.1000-6532.2023.02.029

Citation:

Zhang Hailing. Influence of Vanadium Tailings from Stone Coal on Sintering Brick for Building[J]. Multipurpose Utilization of Mineral Resources, 2023, 44(2): 191-196. doi: 10.3969/j.issn.1000-6532.2023.02.029

Influence of Vanadium Tailings from Stone Coal on Sintering Brick for Building

Zhang Hailing

Department of Civil Engineering and Architecture, Hohhot Vocational College, Hohhot, Inner Mongolia, China

Received Date: 10 September 2021

Publish Date: 25 April 2023

Abstract

Abstract

Fired bricks for building were prepared from the tailings of vanadium extraction from stone coal. The influences of fineness and addition of tailing on the water absorption and compressive strength of samples were investigated. The mechanism of tailoring the phase compositions and microstructures of samples by tailing addition was analyzed by XRD and SEM. The freeze-thaw resistance and utilization safety of the products were tested. The results showed increasing the tailing fineness enhanced the microstructure densification and compressive strength, which firstly increased and then decreased after increasing tailing addition. B3 sample (tailings∶Clay∶fly ash = 30∶30∶40) fired at 1150 ℃ had the compressive strength of ≥35 MPa and the water absorption of ≤ 13%. The comprehensive properties meet the requirements of the Mu30 standard in the《sintered ordinary bricks》(GB/T 5101-2003). XRD and SEM analysis showed that adding 15%~30% tailing was beneficial to the formation of glass phase and promote the production of anorthite as well as anorthosite. Grain and liquid phase are cemented with each other, thus endowing the products with high compressive strength, microstructure densification, and good freeze-thaw resistance.
- Vanadium tailings from stone coal /
- Fired brick for building /
- Microstructure /
- Performance

FullText(HTML)

References

[1]	史政良, 严海军, 周玉娟. 甘肃某石煤钒矿焙烧灰渣综合利用工艺研究[J]. 矿产综合利用, 2020(3):158-163. SHI Z L, YAN H J, ZHOU Y J. Study on comprehensive utilization technology of sulphate roasting ash and slag of vanadium ore from stone coal in Gansu province[J]. Multipurpose Utilization of Mineral Resources, 2020(3):158-163. doi: 10.3969/j.issn.1000-6532.2020.03.027 CrossRef Google Scholar
[2]	Arbi K, Palomo A, Fernández-Jiménez A. Alkali-activated blends of calcium aluminate cement and slag/diatomite[J]. Ceramics International, 2018, 39(8):9237-9245. Google Scholar
[3]	Xu X, Lao X, Wu J, et al. Microstructural evolution, phase transformation, and variations in physical properties of coal series kaolin powder compact during firing[J]. Applied Clay Science, 2015, 115:76-86. doi: 10.1016/j.clay.2015.07.031 CrossRef Google Scholar
[4]	焦向科, 张一敏, 陈铁军, 等. 利用低活性钒尾矿制备地聚合物的研究[J]. 非金属矿, 2011, 34(4):1-4. JIAO X K, ZHANG Y M, CHEN T J, et al. Preparation of geopolymer from vanadium tailings with low activity[J]. Nonmetal Minerals, 2011, 34(4):1-4. doi: 10.3969/j.issn.1000-8098.2011.04.001 CrossRef Google Scholar
[5]	罗立群, 王召, 魏金明, 等. 铁尾矿-煤矸石-污泥复合烧结砖的制备与特性[J]. 中国矿业, 2018(3):127-131. LUO L Q, WANG Z, WEI J M, et al. Preparation and characteristics of iron tailings coal gangue sludge composite sintered brick[J]. China Mining, 2018(3):127-131. Google Scholar
[6]	刘俊杰, 梁钰, 曾宇, 等. 利用铁尾矿制备免烧砖的研究[J]. 矿产综合利用, 2020(5):136-141. LIU J J, LIANG Y, ZENG Y, et al. Preparation of baking-free bricks by iron tailings[J]. Multipurpose Utilization of Mineral Resources, 2020(5):136-141. doi: 10.3969/j.issn.1000-6532.2020.05.021 CrossRef Google Scholar
[7]	汪朋, 韩兵强, 柯昌明, 等. 以高钛型高炉渣提钛后尾渣为结合剂的刚玉浇注料性能研究[J]. 钢铁钒钛, 2016, 37(4):76-82. WANG P, HAN B Q, KE C M, et al. Study on properties of corundum castable with high titanium blast furnace slag tailings as binder[J]. Steel Vanadium and Titanium, 2016, 37(4):76-82. doi: 10.7513/j.issn.1004-7638.2016.04.015 CrossRef Google Scholar
[8]	刘强, 潘志华, 李庆彬, 等. 钙长石系轻质隔热砖的制备及钙长石形成过程[J]. 硅酸盐通报, 2010, 29(6):1269-1274. LIU Q, PAN Z H, LI Q B, et al. Preparation of anorthite series lightweight thermal insulation brick and formation process of anorthite[J]. Silicate Bulletin, 2010, 29(6):1269-1274. doi: 10.16552/j.cnki.issn1001-1625.2010.06.027 CrossRef Google Scholar
[9]	林亚梅, 李翠伟, 汪长安. 莫来石含量对钙长石/莫来石复相多孔陶瓷组织结构与性能的影响[J]. 无机材料学报, 2011, 26(10):1095-1100. LIN Y M, LI C W, WANG C A. Effect of mullite content on microstructure and properties of anorthite/mullite multiphase porous ceramics[J]. Acta Inorganic Materials, 2011, 26(10):1095-1100. doi: 10.3724/SP.J.1077.2011.01095 CrossRef Google Scholar
[10]	李亮, 彭富昌. 浇注法制备提钒尾渣多孔陶瓷试验研究[J]. 钢铁钒钛, 2017, 3(38):84-88. LI L, PENG F C. Experimental study on preparation of porous ceramics from vanadium extraction tailings by casting method[J]. Steel Vanadium and Titanium, 2017, 3(38):84-88. Google Scholar