Preparation and Characterization of Sericite Modified by Macromolecular Coupling Agent KH570-g-PLA

ZHANG Zhen; HU Yingmo; PANG Baobao; WU Shasha; CUI Kui; GUO Sufang

doi:10.13779/j.cnki.issn1001-0076.2022.04.005

2022 Vol. 42, No. 4

Article Contents

Article navigation > Conservation and Utilization of Mineral Resources > 2022 > 42(4): 45-50

Next Article Previous Article

ZHANG Zhen, HU Yingmo, PANG Baobao, WU Shasha, CUI Kui, GUO Sufang. Preparation and Characterization of Sericite Modified by Macromolecular Coupling Agent KH570-g-PLA[J]. Conservation and Utilization of Mineral Resources, 2022, 42(4): 45-50. doi: 10.13779/j.cnki.issn1001-0076.2022.04.005

Citation:

ZHANG Zhen, HU Yingmo, PANG Baobao, WU Shasha, CUI Kui, GUO Sufang. Preparation and Characterization of Sericite Modified by Macromolecular Coupling Agent KH570-g-PLA[J]. Conservation and Utilization of Mineral Resources, 2022, 42(4): 45-50. doi: 10.13779/j.cnki.issn1001-0076.2022.04.005

Preparation and Characterization of Sericite Modified by Macromolecular Coupling Agent KH570-g-PLA

1.
School of Materials Science and Technology, China University of Geosciences(Beijing), Beijing 100083, China
2.
Beijing Key Laboratory of Material Utilization of Nonmetallic Minerals and Solid Waste Resources, Beijing 100083, China
3.
National Laboratory of Rock and Mineral Materials, Beijing 100083, China

More Information

Corresponding author: HU Yingmo, huyingmo@cugb.edu.cn

Received Date: 14 April 2022

Publish Date: 25 August 2022

Abstract

Abstract

The macromolecular coupling agent KH570-g-PLA modified sericite were prepared by one-step composite modification process. The effects on the sericite surface modification efficiency of modifier dosage, reaction time and reaction temperature were investigated with the parameters of turbidity, and contact angle of sericite before and after modification, and the optimizational surface modification conditions of sericite were obtained.The optimal technological conditions of KH570-g-PLA modified sericite were that the 10% of PLA was reacted with sericite at 110℃ for 4 h. The turbidity is 809 NTU and the contact Angle is 66°. Compared with unmodified sericite, its turbidity increased by 196%, and contact angle increased by 285%. The coupling agent KH570-G-PLA was successfully coupled to the surface of sericite. And the KH570-g-PLA modified sericite had a smaller crystal size, seldom agglomeration phenomenon, better dispersibility and hydrophobicity, lower crystallinity and the higher heat resistance temperature (about 705℃).
- sericite /
- polylactic acid /
- KH570 /
- KH570-g-PLA /
- graft copolymerization /
- coupling effect

FullText(HTML)

References

[1]	LIANG Y, YANG D, YANG T, et al. The stability of intercalated sericite by cetyl trimethylammonium ion under different conditions and the preparation of sericite/polymer nanocomposites[J]. Polymers, 2019, 11(5): 900-911. doi: 10.3390/polym11050900 CrossRef Google Scholar
[2]	岳晋充. 云母表面改性方法综述[J]. 科技创新与应用, 2015, 1(31): 7-8. Google Scholar YUE J C. Review on surface modification methods of mica[J]. Science & Technology Innovation and Application, 2015, 1(31): 7-8. Google Scholar
[3]	兰黄鲜. 云母粉在高分子材料改性中的研究进展[J]. 当代化工, 2011, 40(2): 177-179. doi: 10.3969/j.issn.1671-0460.2011.02.022 CrossRef Google Scholar LAN H X. Research progress of mica powder in the modification of polymer materials[J]. Contemporary Chemical Industry, 2011, 40(2): 177-179. doi: 10.3969/j.issn.1671-0460.2011.02.022 CrossRef Google Scholar
[4]	LISICHKIN G, OLENIN A. Hydrophobization of inorganic materials by chemical modification of the surface[J]. Russian Journal of Applied Chemistry, 2020, 93(1): 1-13. Google Scholar
[5]	尚丽娜, 王如寅, 关庆文, 等. 聚乳酸纳米填充改性的研究进展[J]. 化工新型材料, 2009, 37(9): 21-23+51. doi: 10.3969/j.issn.1006-3536.2009.09.007 CrossRef Google Scholar SHANG L N, WANG R Y, GUAN Q W, et al. Research progress of polylactic acid nanofilling modification[J]. New Chemical Materials, 2009, 37(9): 21-23+51. doi: 10.3969/j.issn.1006-3536.2009.09.007 CrossRef Google Scholar
[6]	JAIN S, MISRA M, MOHANTY A, et al. Thermal, mechanical and rheological behavior of poly(lactic acid)/talc composites[J]. Journal of Polymers and the Environment, 2012, 20(4): 1027-1037. doi: 10.1007/s10924-012-0500-z CrossRef Google Scholar
[7]	HE H, LIU B, XUE B, et al. Study on structure and properties of biodegradable PLA/PBAT/organic-modified MMT nanocomposites[J]. Journal of Thermoplastic Composite Materials, 2019, 2: 1-18. Google Scholar
[8]	JIA S, WANG Z, ZHU Y, et al. Composites of poly(lactic) acid/thermoplastic polyurethane/mica with compatibilizer: morphology, miscibility and interphase[J]. RSC Advances, 2015, 5(120): 98915-98924. doi: 10.1039/C5RA17938F CrossRef Google Scholar
[9]	钟振彪. 绢云母的表面改性及其高分子复合材料性能研究[D]. 合肥: 合肥工业大学, 2011. Google Scholar Zhong Z B. Study on surface modification of sericite and properties of polymer composites[D]. Hefei: Hefei University of Technology, 2011. Google Scholar
[10]	CHEN K, LI P, LI X, et al. Effect of silane coupling agent on compatibility interface and properties of wheat straw/polylactic acid composites[J]. International Journal of Biological Macromolecules, 2021, 182: 2108-2116. doi: 10.1016/j.ijbiomac.2021.05.207 CrossRef Google Scholar
[11]	杨琳强, 金立维. 聚乳酸接枝硅烷偶联剂的制备及对聚乳酸/木粉复合材料的影响[J]. 高分子材料科学与工程, 2016, 32(7): 125-130. Google Scholar YANG L Q, JIN L W. Preparation of poly (lactic acid) grafted silane coupling agent and its effect on poly (lactic acid)/wood powder composites[J]. Polymer Materials Science and Engineering, 2016, 32(7): 125-130. Google Scholar
[12]	DUAN J, FAN C, LI Y, et al. Preparation and characterization of the covalent-integrated poly(lactic acid) and scrap leather fiber composites[J]. Journal of Shanghai Jiaotong University (Science), 2012, 17(5): 586-592. Google Scholar
[13]	韩金光, 李珠, 王亮, 等. 膨胀珍珠岩的复合改性工艺及其对混凝土性能的影响[J]. 新型建筑材料, 2016, 43(10): 98-101. Google Scholar HAN J G, LI Z, WANG L, et al. Composite modification process of expanded perlite and its effect on concrete properties[J]. New Building Materials, 2016, 43(10): 98-101. Google Scholar
[14]	赵志鸿, 张廷友, 吕召胜, 等. 超高分子量聚乙烯加工改性研究进展[J]. 工程塑料应用, 2012, 40(1): 99-102. Google Scholar ZHAO Z H, ZHANG T Y, LU Z S, et al. Progress in processing and modification of ultra-high molecular weight polyethylene. Engineering Plastics Application, 2012, 40(1): 99-102. Google Scholar
[15]	汪磊, 周艳, 贾德民. 橡胶/有机蒙脱土纳米复合材料的研究——不同改性工艺的影响[J]. 弹性体, 2002, 1(4): 20-23. Google Scholar WANG L, ZHOU Y JIA D M. Study on rubber/organic montmorillonite nanocomposites: Influence of different modification processes[J]. Elastomers, 2002, 1(4): 20-23. Google Scholar
[16]	REN H, ZHU J, BI Y, et al. One-step fabrication of transparent hydrophobic silica aerogels via in situ surface modification in drying process[J]. Journal of Sol-Gel Science and Technology, 2016, 80(3): 1-7. Google Scholar
[17]	易宁波, 姜波, 黄玉东, 等. 绢云母改性及其在高分子材料中的应用进展[J]. 化学与黏合, 2010, 32(5): 47-49. Google Scholar YI N B, JIANG B, HUANG Y D, et al. Modification of sericite and its Application in polymer Materials[J]. Chemistry and Adhesives, 2010, 32(5): 47-49. Google Scholar
[18]	PENG L. Polymer modified clay minerals: A review[J]. Applied Clay Science, 2007, 38(1/2): 64-76. Google Scholar