Experimental Study on Leaching of High-iron Zinc Calcine

GUO Jialin; SHI Juanning; WANG Zhiyu

doi:10.13779/j.cnki.issn1001-0076.2021.03.008

2021 Vol. 41, No. 3

Article Contents

Article navigation > Conservation and Utilization of Mineral Resources > 2021 > 41(3): 56-59

Next Article Previous Article

GUO Jialin, SHI Juanning, WANG Zhiyu. Experimental Study on Leaching of High-iron Zinc Calcine[J]. Conservation and Utilization of Mineral Resources, 2021, 41(3): 56-59. doi: 10.13779/j.cnki.issn1001-0076.2021.03.008

Citation:

GUO Jialin, SHI Juanning, WANG Zhiyu. Experimental Study on Leaching of High-iron Zinc Calcine[J]. Conservation and Utilization of Mineral Resources, 2021, 41(3): 56-59. doi: 10.13779/j.cnki.issn1001-0076.2021.03.008

Experimental Study on Leaching of High-iron Zinc Calcine

1.
Shangluo University College of Chemical Engineering and Modern Materials, Shangluo 726000, China
2.
Shaanxi Key Laboratory of Comprehensive Utilization of Tailings Resources, Shangluo 726000, China

Received Date: 11 April 2021

Publish Date: 25 June 2021

Abstract

Abstract

During the leaching of high-iron zinc calcine, the leaching of Zn will also lead to the dissolution of impurity Fe, affecting subsequent production and increasing economic costs. To solve this problem, the zinc calcine from an enterprise was taken as the research object. Through the study of The factors affecting the leaching rates of Zn and Fe such as stirring speed, leaching time, initial acidity and leaching temperature were analyzed. The leaching process was optimized. So as to improve the leaching rate of Zn and reduce the leaching rate of Fe. The results showed that under the conditions of leaching temperature of 60 ℃, initial sulfuric acid concentration of 120 g/L, liquid-solid mass ratio of 10:1, stirring speed of 500 r/min and leaching time of 60 min, higher Zn leaching rate and lower Fe leaching rate could be obtained. At this time the Zn leaching rate was 88.5%, and the Fe leaching rate was 10.3%.
- zinc calcine /
- zinc hydrometallurgy /
- leaching

FullText(HTML)

References

[1]	江少卿, 徐毅, 孙尚信, 等. 全球铅锌矿资源分布[J]. 地质与资源, 2020, 29(3): 224-232. doi: 10.3969/j.issn.1671-1947.2020.03.003 CrossRef Google Scholar
[2]	杨金林, 肖汉新, 罗美秀, 等. 锌焙砂浸出锌、铁试验研究[J]. 广西大学学报(自然科学版), 2017, 42(2): 646-654. Google Scholar
[3]	彭兵, 林冬红, 刘恢, 等. 高铁锌焙砂还原焙烧-碱浸工艺[J]. 中国有色金属学报, 2017, 27(2): 423-429. Google Scholar
[4]	程文军, 秦法聪, 刘营. 控制锌焙砂可溶硫含量的研究与实践[J]. 世界有色金属, 2016(16): 74-75. Google Scholar
[5]	焦晓斌, 段小维, 段宏志. 锌焙砂浸出过程中两渣分离的探索与实践[J]. 中国有色冶金, 2016, 45(3): 6-9+34. Google Scholar
[6]	彭兵, 林冬红, 刘恢, 等. 高铁锌焙砂还原焙烧-碱浸工艺[J]. 中国有色金属学报, 2017, 27(2): 423-429. Google Scholar
[7]	闫缓, 柴立元, 彭兵, 等. 高铁锌焙砂还原焙烧-酸性浸出选择性分离铁锌研究[J]. 安全与环境学报, 2015, 15(5): 277-281. Google Scholar
[8]	韩俊伟, 刘维, 覃文庆, 等. 高铁锌焙砂选择性还原焙烧-两段浸出锌[J]. 中国有色金属学报, 2014, 24(2): 511-518. Google Scholar
[9]	李敦华. 湿法炼锌浸出渣含锌的影响因素分析与控制[J]. 中国有色冶金, 2019, 48(6): 13-16. Google Scholar
[10]	罗美秀. 锌焙砂硫酸浸出及制取铁酸锌试验研究[D]. 南宁: 广西大学, 2015. Google Scholar